S3TA Flame Retardant Dual Wall Heat Shrink Tube
S3TA
$0.00
Introduction Thin wall polyolefin heat-shrinkable tube, with adhesive liner, flame-retardant (colors). Suitable for waterproof sealing and insulation protection of automotive wire splices, terminals and components. Length can be...
Introduction
Thin wall polyolefin heat-shrinkable tube, with adhesive liner, flame-retardant (colors). Suitable for waterproof sealing and insulation protection of automotive wire splices, terminals and components. Length can be customized.
Features
Operating temperature: -40 to 105°C
Minimum full recovery temperature: 125°C
Shrink ratio: 3:1 & 4:1
Environmental friendly, RoHS & ELV compliant
Standard Color: Black & Clear
Dimensions
| Part No. S3TA |
As supplied(mm) | After recovered(mm) | ||||
| Inner diameter D(min.) |
Wall thickness T(nom.) |
Inner diameter d(max.) |
Wall thickness t(nom.) |
Adhesive Wall thicknesst1(nom.) |
||
| Shrink ratio 4:1 | ||||||
| 4.0/1.0 | 4.0 | 0.45 | 1.0 | 1.0 | 0.5 | |
| 6.0/1.5 | 6.0 | 0.60 | 1.5 | 1.4 | 0.7 | |
| 8.0/2.0 | 8.0 | 0.60 | 2.0 | 1.6 | 0.9 | |
| 9.0/2.3 | 9.0 | 0.65 | 2.3 | 1.8 | 1.0 | |
| 11.0/2.4 | 11.0 | 0.65 | 2.4 | 2.0 | 1.1 | |
| 12.0/3.0 | 12.0 | 0.80 | 3.0 | 2.2 | 1.2 | |
| 14.0/3.5 | 14.0 | 0.80 | 3.5 | 2.3 | 1.3 | |
| 16.0/4.0 | 16.0 | 0.80 | 4.0 | 2.4 | 1.4 | |
| 18.0/4.5 | 18.0 | 0.80 | 4.5 | 2.6 | 1.4 | |
| Shrink ratio 3:1 | ||||||
| 3.2/1.0 | 3.2 | 0.45 | 1.0 | 1.0 | 0.45 | |
| 4.8/1.6 | 4.8 | 0.50 | 1.6 | 1.1 | 0.5 | |
| 6.4/2.1 | 6.4 | 0.50 | 2.1 | 1.2 | 0.5 | |
| 7.9/2.6 | 7.9 | 0.50 | 2.6 | 1.3 | 0.6 | |
| 9.5/3.2 | 9.5 | 0.50 | 3.2 | 1.4 | 0.6 | |
| 12.7/4.2 | 12.7 | 0.60 | 4.2 | 1.6 | 0.7 | |
| 15.0/5.0 | 15.0 | 0.65 | 5.0 | 1.8 | 0.8 | |
| 19.1/6.0 | 19.1 | 0.70 | 6.0 | 1.9 | 0.8 | |
Technical Data
| Property | Test method | Requirement | ||||
| Longitudinal change | ASTM D2671 | ≥-10% | ||||
| Tensile strength | ASTM D2671 | ≥10.4 MPa | ||||
| Ultimate elongation | ASTM D2671 | ≥300% | ||||
| Heat Aging(136°℃/168hrs) | ASTM D2671 | |||||
| Tensile Strength | ≥7.3 MPa | |||||
| Ultimate Elongation | ≥200% | |||||
| Water absorption(23°℃/24h) | ASTM D570 | ≤0.5% | ||||
| Low-temperature flexibility(-40℃/4h) | ASTM D2671 | No cracking | ||||
| Heat shock(200℃/4hrs) | ASTM D2671 | No cracking,dripping or flowing ofouterjacket | ||||
| Dielectric strength | ASTM D2671 | ≥12kV/mm | ||||
| Volume resistivity | ASTM D2671 | ≥1.0×10¹⁴Ω.cm | ||||
| Flammability (colors only) | ASTM D2671 | Self-extinguishing within 60S | ||||
| method C | ||||||
| Copper corrosion(136℃/16h) | ASTM D2671 | No corrosion | ||||
| Fluid resistance | ISO(23℃/24hrs) | |||||
| Tensile Strength | Diesel fuel(BS 2869 Class Al) | ≥7.0 MPa | ||||
| Ultimate Elongation |
Hydraulicfluid(MIL-H-5606) Lubricating oil(0-149) |
≥100% | ||||