IDS-LSF Low Smoke Halogen-free Laser Marking Heat Shrink Marker Sleeve
IDS-LSF
$0.00
IDS-LSF Low Smoke Halogen-free Laser Marking Heat Shrink Marker Sleeve Introduction A low-smoke, halogen-free, flame-retardant polyolefin.A laser engraving machine can be used for ensuring permanent identification,abrasion and solvent...
IDS-LSF Low Smoke Halogen-free Laser Marking Heat Shrink Marker Sleeve
Introduction
A low-smoke, halogen-free, flame-retardant polyolefin.A laser engraving machine can be used for ensuring permanent identification,abrasion and solvent resistance.Printable patches and continuous tubes both are available.
Features
Operating temperature: -55 to 125°C
Minimum full recovery temperature: 135°C
Shrink ratio: 2:1
Halogen-free, RoHS compliant
Compliant Standard EN45545-2 2013 R22/R23
Standard Color: See the below for details
Dimension
| Part No. IDS-LSF |
As supplied(mm) | After recovered(mm) | |||||||
| Inner diameter D(min.) |
Sleeve Flattened Width W(min. |
Sleeve Progression (nom.) |
Inner diameter d(max.) |
Wall thickness |
|||||
| IDS-LSF-M-2X-2.4-* | 2.4 | 4.3 | 12.7 | 1.2 | 0.50±0.10 | ||||
| IDS-LSF-M-2X-3.2-* | 3.2 | 6.5 | 12.7 | 1.6 | 0.50±0.10 | ||||
| IDS-LSF-M-2X-4.8- | 4.8 | 8.9 | 12.7 | 2.4 | 0.51±0.11 | ||||
| IDS-LSF-M-2X-6.4-* | 6.4 | 11.0 | 16.9 | 3.2 | 0.65±0.15 | ||||
| IDS-LSF-M-2X-9.5-* | 9.5 | 15.7 | 25.4 | 4.8 | 0.65±0.15 | ||||
| IDS-LSF-M-2X-12.7-* | 12.7 | 20.7 | 29.6 | 6.4 | 0.65±0.15 | ||||
| IDS-LSF-M-2X-19.0-* | 19.1 | 30.7 | 42.3 | 9.5 | 0.75±0.15 | ||||
| IDS-LSF-M-2X-25.4-* | 25.4 | 41.1 | 50.8 | 12.7 | 0.90±0.15 | ||||
| IDS-LSF-M-2X-38.1-* | 38.1 | 61.0 | 72.0 | 19.1 | 1.00±0.20 | ||||
| IDS-LSF-M-2X-50.8-* | 50.8 | 80.0 | 101.6 | 25.4 | 1.00±0.20 | ||||
Technical Data
| Property | Test Method | Requirement | |||||||
| Longitudinal change | ASTM D 2671 | -10%/+5% | |||||||
| Tensile Strength | ASTM D 2671 | ≥10.3MPa | |||||||
| Ultimate Elongation | ASTM D 2671 | ≥200% | |||||||
| Heat Aging(136°C/168h) | ASTM D 2671 | ||||||||
| Ultimate Elongation | ≥100% | ||||||||
| Low-temperature flexibility (-55°℃/4h) | ASTM D 2671 | No cracking | |||||||
| Heat shock(200°℃/4h) | ASTM D2671 | No cracking,dripping or flowing | |||||||
| Water absorption(23℃/24h) | ASTM D 2671 | ≤1.0% | |||||||
| Dielectric voltage Withstand | ASTMD2671 | 2500V,60s No breakdown | |||||||
| Dielectric strength | ASTM D 2671 | ≥19.7kV/mm | |||||||
| Volume resistivity | ASTMD 2671 | ≥1.0×10¹⁴Ω.cm | |||||||
| Flammability | ASTMD2671 Method C | 60second maximum burning duration | |||||||
| Coppereffect(136°C/16h) | ASTMD2671 | No corrosion | |||||||
| Print perfomance | SAE AS5942 | Pass(legible after 50 rubs) | |||||||
| MIL-STD-202 | Pass(legible after 30 strokes) | ||||||||
| Fluid resistance(23°C/24h) | SAE AS5942 | Mark is legible | |||||||