C105 Semi-Conductive/Insulation Double Layer Heat Shrink Tube
C105
$0.00
C105 Semi-Conductive/Insulation Double Layer Heat Shrink Tube Introduction Co-extrusion design,semi-conductive/insulation double layer heat shrink tube.Suitable for insulation protection of power cable joint under 36kV. Features Operating temperature: -55...
C105 Semi-Conductive/Insulation Double Layer Heat Shrink Tube
Introduction
Co-extrusion design,semi-conductive/insulation double layer heat shrink tube.Suitable for insulation protection of power cable joint under 36kV.
Features
Operating temperature: -55 to 105°C
Minimum fully recovery temperature: 135°C
Voltage class: 6kV ~ 36kV
Halogen-free, RoHS compliant, Heavy wall
Semi-conductive / insulation double layer
Standard Color: Black (outer layer) / Red(inner layer)
Dimension
| Part No. C105 |
Assupplied(mm) nner diameter D(min.) |
After recovered(mm) | Standard length (m/pc) |
||||||
| Inner diameter d(max.) |
Wall thickness t(nom.) |
||||||||
| 38/13 | 38 | 13 | 5.0 | ≤1.22 | |||||
| 45/17 | 45 | 17 | 5.5 | ≤1.22 | |||||
| 50/20 | 50 | 20 | 5.5 | ≤1.22 | |||||
| 55/23 | 55 | 23 | 5.5 | ≤1.22 | |||||
| 65/25 | 65 | 25 | 6.0 | ≤1.22 | |||||
| 75/30 | 75 | 30 | 6.0 | ≤1.22 | |||||
| 85/35 | 85 | 35 | 6.0 | ≤1.22 | |||||
| 95/40 | 95 | 40 | 6.2 | ≤1.22 | |||||
| 115/50 | 115 | 50 | 6.3 |
≤1.22 |
|||||
Technical Data
| Property | Test Method | Requirement | |||||||
| Outer Layer(Semi-Conductive,Black) | |||||||||
| Tensile Strength | ASTM D2671 | ≥12MPa | |||||||
| Ultimate Elongation | ASTM D2671 | ≥270% | |||||||
| Heat Aging(158℃/168h) | ASTM D2671 | ||||||||
| Tensile Strength | ≥10 MPa | ||||||||
| Ultimate Elongation | ≥250% | ||||||||
| Water absorption(23C/24h) | ASTM D2671 | ≤0.5% | |||||||
| Low-temperature flexibility (-40℃/4h) | ASTM D2671 | No cracking | |||||||
| Heat shock(200°℃/4h) | ASTM D2671 | No dripping orflowing | |||||||
| Volume resistivity | ASTM D2671 | ≤1×10+Q.cm | |||||||
| Inner Layer (Insulation,red) | |||||||||
| Tensile Strength | ASTM D2671 | ≥12MPa | |||||||
| Ultimate Elongation | ASTM D2671 | ≥350% | |||||||
| Heat Aging(136℃/168h) | ASTM D2671 | ||||||||
| Tensile Strength | ≥10 MPa | ||||||||
| Ultimate Elongation | ≥270% | ||||||||
| Water absorption(23C/24h) | ASTM D2671 | ≤0.5% | |||||||
| Low-temperatureflexibility(-40°℃/4h) | ASTM D2671 | No cracking | |||||||
| Heat shock(200℃/4h) | ASTM D2671 | No dripping orflowing | |||||||
| Dielectric strength | ASTM D2671 | ≥15kV/mm | |||||||
| Volume resistivity | ASTM D2671 | ≥1×10¹³Q.cm | |||||||