S10 Fluororubber Heat Shrink Tube
$0.00
S10 Fluororubber Heat Shrink Tube Introduction A flexible,cross-linked fluororubber heat shrink tubing used for connecting, insulating, and protecting various types of wires and cables in military equipment requiring...
S10 Fluororubber Heat Shrink Tube
Introduction
A flexible,cross-linked fluororubber heat shrink tubing used for connecting, insulating, and protecting various types of wires and cables in military equipment requiring resistance to high temperatures, oil, and chemical solvents. Ideal for stress relief at terminations or joints, insulation protection or covering of wiring, and encapsulation of electronic components.
Features
Operating temperature: -55 to 200°C
Minimum full recovery temperature: 175°C
Shrink ratio: 2:1
Standard Color: Black (-0)
Compliant Standard GJB 7273-2011
Excellent high-temperature resistance, solvent resistance, oil resistance, and chemical corrosion resistance
Flexible, Flame-retardant, wear resistant
Dimension
| Size | As supplied(mm) | After recovered (mm) |
Unit weight (max.) g/m |
Standard length (m) |
|
| S10 |
Inner diameter D (min.) |
Inner diameter d (max.) |
Wall thickness t |
||
| 2.4/1.2 | 2.4 | 1.2 | 0.60±0.10 | 9.8 | 100 |
| 3.2/1.6 | 3.2 | 1.6 | 0.76±0.13 | 11.8 | 100 |
| 4.8/2.4 | 4.8 | 2.4 | 0.89±0.18 | 17.5 | 100 |
| 6.4/3.2 | 6.4 | 3.2 | 0.89±0.18 | 20.6 | 61 |
| 9.5/4.8 | 9.5 | 4.8 | 0.89±0.18 | 33.7 | 61 |
| 12.7/6.4 | 12.7 | 6.4 | 0.89±0.18 | 60.7 | 61 |
| 15.9/7.9 | 15.9 | 7.9 | 1.07±0.21 | 76 | 61 |
| 19.1/9.5 | 19.1 | 9.5 | 1.07±0.21 | 88.8 | 61 |
| 22.2/11.1 | 22.2 | 11.1 | 1.25±0.30 | 140 | 61 |
| 25.4/12.7 | 25.4 | 12.7 | 1.25±0.30 | 151 | 61 |
| 38.1/19.1 | 38.1 | 19.1 | 1.40±0.38 | 252.3 | 30.5 |
| 50.8/25.4 | 50.8 | 25.4 | 1.65±0.43 | 300.5 | 30.5 |
Technical Data (GJB 7273-2011)
| Property | Test Method | Requirement | |||
| Longitudinal change | -- | -20% ~ 20% | |||
| Restricted Shrinkage | 200°C/30min | No cracking | |||
| Water absorption | 23°C/24h | ≤0.5% | |||
| Tensile Strength | 500mm/min | ≥11.0 MPa | |||
| Ultimate Elongation | 500mm/min | ≥250% | |||
| Heat shock | 300°C/4h | No cracking, dripping or flowing | |||
| Heat Aging Tensile Strength Ultimate Elongation |
250°C/168h |
≥11.0 MPa ≥200% |
|||
| Dielectric strength | -- | ≥7.9kV/mm | |||
| Dielectric withstand | AC 2500V, 60s | No breakdown | |||
| Volume resistivity | -- | ≥1.0×109Ω·cm | |||
| Fluid resistance Tensile Strength Ultimate Elongation |
23°C/24h |
≥ 11.0MPa ≥ 250% |
|||
| Flammability | -- | 60 second maximum burning duration | |||
| Copper corrosion | 175°C/16h | No Corrosion | |||
| Low-temperature flexibility | -55°C/4h | No Cracking | |||
| Thermal cycling Tensile Strength Ultimate Elongation |
-55°C/200°C/10 cycles |
≥ 11MPa ≥ 200% |
|||
| Salt spray test Tensile Strength Ultimate Elongation |
GJB 150.11 |
≥ 11MPa ≥ 200% |
|||
| Damp-heat test Tensile Strength Ultimate Elongation |
GJB 150.9 |
≥ 11MPa ≥ 200% |
|||
| Fungus Resistance | GJB 150.10 | No worse than rating 1 | |||