IDS-LSH Flame-retardant Laser Marking Heat Shrink Marker Sleeve
IDS-LSH
$0.00
IDS-LSH Flame-retardant Laser Marking Heat Shrink Marker Sleeve Introduction High flame-retardant, electrical insulation, chemical resistance.A laser engraving machine can be used for ensuring permanent identification,abrasion and solvent resistance.Printable...
IDS-LSH Flame-retardant Laser Marking Heat Shrink Marker Sleeve
Introduction
High flame-retardant, electrical insulation, chemical resistance.A laser engraving machine can be used for ensuring permanent identification,abrasion and solvent resistance.Printable patches and continuous tubes both are available.
Features
Operating temperature: -55 to 125°C
Minimum full recovery temperature: 135°C
Shrink ratio: 2:1
Environmental friendly, RoHS compliant
Standard Color: See the below for details
Dimension
| Part No. IDS-LSH |
As supplied(mm) | After recovered(mm) | |||
| Inner diameter D(min.) |
Sleeve Flattened Width W(min. |
Sleeve Progression (nom.) |
Inner diameter d(max.) |
Wall thickness t |
|
| IDS-LSH-M-2X-1.6-* | 1.6 | 3.2 | 10.3 | 0.8 | 0.45±0.08 |
| IDS-LSH-M-2X-2.4-* | 2.4 | 4.3 | 12.7 | 1.2 | 0.50±0.10 |
| IDS-LSH-M-2X-3.2-* | 3.2 | 5.8 | 12.7 | 1.6 | 0.50±0.10 |
| IDS-LSH-M-2X-4.8-* | 4.8 | 8.0 | 12.7 | 2.4 | 0.55±0.11 |
| IDS-LSH-M-2X-6.4-* | 6.4 | 10.7 | 16.9 | 3.2 | 0.55±0.11 |
| IDS-LSH-M-2X-9.5-* | 9.5 | 15.5 | 25.4 | 4.8 | 0.60±0.12 |
| IDS-LSH-M-2X-12.7-* | 12.7 | 20.4 | 27.9 | 6.4 | 0.60±0.12 |
| IDS-LSH-M-2X-19.1-* | 19.1 | 30.5 | 38.1 | 9.5 | 0.70±0.15 |
| IDS-LSH-M-2X-25.4-* | 25.4 | 40.4 | 48.3 | 12.7 | 0.70±0.15 |
| IDS-LSH-M-2X-38.1-* | 38.1 | 60.3 | 70.0 | 19.1 | 0.70±0.15 |
| IDS-LSH-M-2X-50.8-* | 50.8 | 80.0 | 96.5 | 25.4 | 0.73±0.15 |
| IDS-LSH-M-2X-76.2-* | 76.2 | 114.3 | 137.2 | 38.1 | 0.73±0.15 |
Technical Data
| Property | Test Method | Requirement | |
| Longitudinal Change | ASTM D2671 | -10%/+5% | |
| Restricted Shrinkage | 158°℃/30min | No cracking | |
| Water Absorption | 23°℃/24h | ≤0.5% | |
| Tensile Strength | 500mm/min | ≥10.4MPa | |
| Utimate Elongation | 500mm/min | ≥200% | |
| Heat shock | 200°℃/4h | No cracking,dripping or flowing | |
| Mark Identifiability | After erasng 50 times with an eraser | ||
| in one direction,mark is legible | |||
| Heat Aging | 158°C/168h | ≥200% | |
| Ultimate Elongation | After erasing50 times with an eraserin one | ||
| Mark Identifiability direction,mark islegible | |||
| Color Stability | 158℃/24h | No fading or discoloration | |
| Print Perfomance | Surface characters are erased | Mark is legible | |
| 50 times in one direction or30 | |||
| times back and forth | |||
| Dielectric Strength | ASTM D2671 | ≥19.7kV/mm | |
| Dielectric Voltage Withstand | AC 2500V,60s | No breakdown | |
| Volume Resistivity | ASTM D2671 | ≥1.0×10¹⁴Ω.cm | |
| Fluid resistance | 23°℃/24h | ||
| Tensile Strength | ≥6.9MPa | ||
| Dielectric Strength | ≥15.8kV/mm | ||
| Mark Identifiability | After erasing 50 times with an eraser | ||
| in one direction,markis legible | |||
| Flammability | ASTM D2671Method c | 60 second maximum burning duration | |
| Copper Effect | 158℃/16h | No corrosion | |
| Low-temperature Flexibility | -55°℃/4h | No cracking | |