Introduction Cross-linked polyolefin,with adhesive liner and heat sensitive paint.It has good air tightness, temperature cycle resistance, and chemical corrosion resistance.Suitable for sealing and protection of the incoming and...
Introduction
Cross-linked polyolefin,with adhesive liner and heat sensitive paint.It has good air tightness, temperature cycle resistance, and chemical corrosion resistance.Suitable for sealing and protection of the incoming and outgoing lines of the fiber optic dome closure.
Features
Operating temperature: -55 to 125°C
Minimum fully recovery temperature: 115°C
Shrink ratio: 2:1
Halogen-free, RoHS compliant
Standard Color: Black
Dimension
| Part No. S3PS |
As supplied(mm) Inner diameter D(min.) |
After recovered(mm) |
Standard length (mm/pc) |
|||
| Inner diameter d(max.) |
Wall thickness t(nom.) |
|||||
| 28/6 | 28 | 6 | 3.0 | 150/180/200 | ||
| 30/10 | 30 | 10 | 3.0 | 150/180/200 | ||
| 40/10 | 40 | 10 | 3.7 | 150/180/200 | ||
| 65/20 | 65 | 20 | 3.6 | 150/180/200 | ||
| 75/22 | 75 | 22 | 3.7 | 150/180/200 | ||
| 85/25 | 85 | 25 | 3.8 | 150/180/200 | ||
| 35/10 | 35 | 10 | 3.0 | 150/180/200 | ||
| 75/20 | 75 | 20 | 3.7 | 150/180/200 | ||
Technical Data
| Property | Test Method | Requirement | ||||
| Heat Shrink tube | ||||||
| Density | ASTM D2671 | 1.0-1.1g/cm³ | ||||
| Operating temperature maximum | IEC216 | 110℃ | ||||
| Longitudinal Change | ASTM D2671 | ±10% | ||||
| Tensile Strength | ASTM D2671 | ≥17 MPa | ||||
| Ultimate Elongation | ASTM D2671 | ≥350% | ||||
| Heat Aging(150℃/168h) | ASTM D2671 | |||||
| Tensile Strength | ≥14 MPa | |||||
| Ultimate Elongation | ≥270% | |||||
| Water absorption(23°C/24h) | ASTM D2671 | ≤0.2% | ||||
| Low-temperature flexibility (-40℃/4h) | ASTM D2671 | No cracking | ||||
| Heat shock(200°℃/4h) | ASTM D2671 | No dripping or flowing | ||||
| Environmental stress cracking resistance | ASTM D1693 | No cracking | ||||
| Dielectric strength | ASTM D2671 | ≥15kV/mm | ||||
| Volume resistivity | ASTM D2671 | ≥1.0×10¹⁴ Ω ·cm | ||||
| Storage | Outer diameter and longitudinal Change≤2% | |||||
| Discoloration due to heating | Below180℃,thermo-chromaic paint not change color while 250°℃ color-changing complete |
|||||
| Adhesive | ||||||
| Ring-and-Ball Softening Point | GB/T15332.94 | ≥115℃ | ||||
| Viscosity | HG/T 3660-1999 | ≥50000mPa ·S | ||||
| Environmental stress cracking resistance | 50°C/48h | No cracking of heat shrink tube | ||||
| Corrosion of copper,aluminum and steel | 120℃/16h | No corrosion | ||||