S6-T Polyurethane Elastomer Heat Shrink Tube Introduction Cross-linked polyurethane elastomer, flexible, heat shrinkable tubing. Used for military and commercial equipment to protect wire and cable from diesel fuels,...
S6-T Polyurethane Elastomer Heat Shrink Tube
Introduction
Cross-linked polyurethane elastomer, flexible, heat shrinkable tubing. Used for military and commercial equipment to protect wire and cable from diesel fuels, hydraulic fluids, lubrication oils and abrasion .
Features
Operating temperature: -55 to 125°C
Minimum full recovery temperature: 150°C
Shrink ratio: 2:1
Standard Color: Black (-0)
Compliant Standard GJB 7274-2011
Good resistance to wear resistance, lubricating oil and hydraulic oil
Flexible, Flame-retardant
Dimension
| PartNo. S6-T S6-TTW |
As supplied(mm) Inner diameter D(min.) |
After recovered(mm) | Unit weight (max.) g/m |
Standard Length (m) |
||
| Inner diameter d(max.) |
Wall thickness t |
|||||
| Normal S6-T | ||||||
| 1.6/0.85 | 1.6 | 0.85 | 0.40±0.08 | 3.1 | 200 | |
| 2.4/1.2 | 2.4 | 1.2 | 0.51±0.08 | 5.9 | 200 | |
| 3.2/1.6 | 3.2 | 1.6 | 0.76±0.15 | 9.6 | 200 | |
| 4.8/2.4 | 4.8 | 2.4 | 0.84±0.15 | 14.7 | 200 | |
| 6.4/3.2 | 6.4 | 3.2 | 0.89±0.15 | 19.3 | 200 | |
| 9.5/4.8 | 9.5 | 4.8 | 1.02±0.20 | 31.5 | 122 | |
| 12.7/6.4 | 12.7 | 6.4 | 1.22±0.20 | 42.5 | 122 | |
| 15.9/7.9 | 15.9 | 7.9 | 1.32±0.28 | 57.5 | 61 | |
| 19.1/9.5 | 19.1 | 9.5 | 1.45±0.28 | 80.1 | 61 | |
| 22.2/11.1 | 22.2 | 11.1 | 1.55±0.28 | 98.5 | 61 | |
| 25.4/12.7 | 25.4 | 12.7 | 1.78±0.28 | 120.0 | 61 | |
| 31.8/15.9 | 31.8 | 15.9 | 2.20±0.41 | 172.5 | 30.4 | |
| 38.1/19.1 | 38.1 | 19.1 | 2.41±0.41 | 243.0 | 30.4 | |
| 50.8/25.4 | 50.8 | 25.4 | 2.79±0.41 | 342.0 | 30.4 | |
| S6-TTW(Thinner Wall) | ||||||
| 1.6/0.85 | 1.6 | 0.85 | 0.40±0.08 | 3.1 | 200 | |
| 2.4/1.2 | 2.4 | 1.2 | 0.51±0.08 | 5.9 | 200 | |
| 3.2/1.6 | 3.2 | 1.6 | 0.51±0.08 | 7.0 | 200 | |
| 4.8/2.4 | 4.8 | 2.4 | 0.51±0.08 | 9.6 | 200 | |
| 6.4/3.2 | 6.4 | 3.2 | 0.64±0.08 | 15.6 | 200 | |
| 9.5/4.8 | 9.5 | 4.8 | 0.64±0.08 | 22.2 | 122 | |
| 12.7/6.4 | 12.7 | 6.4 | 0.64±0.08 | 27.0 | 122 | |
| 15.9/7.9 | 15.9 | 7.9 | 0.76±0.15 | 37.6 | 61 | |
| 19.1/9.5 | 19.1 | 9.5 | 0.76±0.15 | 47.2 | 61 | |
| 22.2/11.1 | 22.2 | 11.1 | 0.89±0.15 | 60.2 | 61 | |
| 25.4/12.7 | 25.4 | 12.7 | 0.89±0.15 | 67.6 | 61 | |
| 31.8/15.9 | 31.8 | 15.9 | 1.02±0.20 | 90.4 | 30.4 | |
| 38.1/19.1 | 38.1 | 19.1 | 1.02±0.20 | 115.4 | 30.4 | |
| 50.8/25.4 | 50.8 | 25.4 | 1.14±0.20 | 157.9 | 30.4 | |
Technical Data(GJB7274-2011)
| Property | Test Method | Requirement | ||
| Density | ASTM D792 | ≤1.50g/cm³ | ||
| Longitudinal change | 一 | -10%~10% | ||
| Restricted Shrinkage | 200°℃/30min | No cracking | ||
| Water absorption | 23°C/24h | ≤2.0% | ||
| Tensile Strength | 500mm/min | ≥11.7MPa | ||
| Ultimate Elongation | 500mm/min | ≥250% | ||
| Heat shock | 200°℃/4h | No cracking,dripping or flowing | ||
| Heat Aging | 150°℃/168h | |||
| Tensile Strength | ≥10.4MPa | |||
| Ultimate Elongation | ≥200% | |||
| Dielectric strength | 一 | ≥11.9k/mm | ||
| Dielectric withstand | AC2500V,60s | No breakdown | ||
| Volume resistivity | 一 | ≥1.0×10°Ω ·cm | ||
| Fluid resistance | 23°C/24h | |||
| Tensile Strength | ≥Not lessthan 70%value before test | |||
| Ultimate Elongation | ≥100% | |||
| Flammability | 一 | ≤60S burning duration | ||
| Copper corrosion | 135°C/16h | No Corrosion | ||
| Low-temperature flexibilty | -55℃/4h | No Cracking | ||
| Thermal cycling | -55C/120℃ | |||
| Tensile Strength | /10cycles | Not less than 70%value before test | ||
| Utimate Elongation | ≥100% | |||
| Salt spray test | GJB 150.11 | |||
| Tensile Strength | Not less than 70%value before test | |||
| Ultimate Elongation | ≥100% | |||
| Damp-heat test | GJB150.9 | |||
| Tensile Strength | Not less than 70%value before test | |||
| Ultimate Elongation | ≥100% | |||
| Fungus Resistance | GJB150.10 | Not worse than rating 1 | ||