S5-PVDF-175 175℃ PVDF Thin Wall Heat Shrink Tube
S5-PVDF
$0.00
S5-PVDF-175 175℃ PVDF Thin Wall Heat Shrink Tube Introduction A flame-retardant, semirigid, very thin wall insulation tube. Suitable for applications requiring high-temperature performance, outstanding abrasion and cut-through resistance,...
S5-PVDF-175 175℃ PVDF Thin Wall Heat Shrink Tube
Introduction
A flame-retardant, semirigid, very thin wall insulation tube. Suitable for applications requiring high-temperature performance, outstanding abrasion and cut-through resistance, superior chemical and solvent resistance properties. Transparent tubing for easy see-through inspection.
Features
Operating temperature: -55 to 175°C
Minimum full recovery temperature: 175°C
Shrink ratio: 2:1
Environmental friendly, RoHS compliant
Standard Color: Clear
Excellent flame retardant
Dimension
| PartNo. S5-PVDF-175 |
As supplied(mm) lnner diameter D(min.) |
After recovered(mm) | ||
| Inner diameter d(max.) |
Wall thickness t(nom.) |
|||
| 1.2/0.6 | 1.2 | 0.6 | 0.25 | |
| 1.6/0.8 | 1.6 | 0.8 | 0.25 | |
| 2.4/1.2 | 2.4 | 1.2 | 0.25 | |
| 3.2/1.6 | 3.2 | 1.6 | 0.25 | |
| 4.8/2.4 | 4.8 | 2.4 | 0.25 | |
| 6.4/3.2 | 6.4 | 3.2 | 0.30 | |
| 9.5/4.8 | 9.5 | 4.8 | 0.30 | |
| 12.7/6.4 | 12.7 | 6.4 | 0.30 | |
| 19.1/9.5 | 19.1 | 9.5 | 0.43 | |
| 25.4/12.7 | 25.4 | 12.7 | 0.48 | |
| 38.1/19.1 | 38.1 | 19.1 | 0.51 | |
| 50.8/25.4 | 50.8 | 25.4 | 0.58 | |
Technical Data
| Property | Test Method | Requirement | |
| Density | ASTM D2671 | ≤1.80g/cm³ | |
| Longitudinal Change | ASTM D2671 | -10%to+5% | |
| Tensile strength | ASTM D2671 | ≥34.5 MPa | |
| Ultimate elongation | ASTM D2671 | ≥150% | |
| Secant modulus (expanded) | ASTM D2671 | ≥690 MPa | |
| Clarity Stability(175℃/24h) | ASTM D2671 | The markings in the sample are clearly visible | |
| Low-temperature flexibility(-55°℃/4h) | AMS-DTL-23053/8 | No cracking | |
| Heat shock(300°℃/4h) | AMS-DTL-23053 | No dripping,flowing or cracking | |
| Heat resistance(250°℃/168h) | ASTM D2671 | ||
| Ultimate elongation | ≥50% | ||
| Vacuum Outgassing | ASTME595 | ||
| TML(Total Mass Loss) | ≤1.0% | ||
| VCM(Volatile Condensable Material) | ≤0.1% | ||
| Dielectric strength | ASTM D2671 | ||
| Sizes 1.2/0.6through 12.7/6.4 | ≥31.5kV/mm | ||
| Sizes 19.1/9.5through 76.2/38.1 | ≥23.6kV/mm | ||
| Volume resistivity | ASTM D2671 | ≥1×10¹³Ω ·cm | |
| Water absorption(23°℃/24h) | ASTM D2671 | ≤0.5% | |
| Copper mirror corrosion(175°℃/16h) | ASTMD2671 ProcedureA | Non-Corrosive | |
| Copper Contact(175℃/168h) | ASTMD 2671Procedure B | No pitting or blackening of copper | |
| Ultimate elongation | ASTM D2671 | ≥100% | |
| Flammability(Average Time of Burning | )UL224 | ≤15 seconds | |
| Fungus Resistance | ISO 846 Method B | ||
| Tensile Strength | ASTM D2671 | ≥34.5 Mpa | |
| Ultimate Elongation | ≥150% | ||
| Dielectric Strength | |||
| Sizes 1.2/0.6 through 12.7/6.4 | ≥31.5kV/mm | ||
| Sizes 19.1/9.5 through 76.2/38.1 | ≥23.6kV/mm | ||
| Fluid Resistance | ASTM D2671 | ||
| 24 hours at 23±3℃(73±5°F) | |||
| JP-8 Fuel(MIL-T-83133) | |||
| Skydrol*500,Hydraulic Fluid(MIL-H-5606) | |||
| Aviation Gasoline 100/130(ASTM D910) | |||
| Salt Water (5%salt) | |||
|
Anti-icing Fluid(AMS1424) Lubricating Oil(MIL-L-7808) |
|||
| Tensile strength | ≥34.5 Mpa | ||
| Dielectric Strength | |||
| Sizes 1.2/0.6 through 12.7/6.4 | ≥27.6kV/mm | ||
| Sizes 19.1/9.5 through 76.2/38.1 | ≥19.7 kV/mm | ||