S13 Low Vacuum Outgassing and Radiation Resistance Heat Shrink Tube
$0.00
S13 Low Vacuum Outgassing and Radiation Resistance Heat Shrink Tube Introduction Flexible cross-linked modified polyolefin heat shrink tube, with radiation resistance, low outgassing in vacuum, flame-retardant.Used for protecting...
S13 Low Vacuum Outgassing and Radiation Resistance Heat Shrink Tube
Introduction
Flexible cross-linked modified polyolefin heat shrink tube, with radiation resistance, low outgassing in vacuum, flame-retardant.Used for protecting components and connections in military and aerospace equipment, effectively achieving radiation resistance and preventing small molecule release and weight loss in low vacuum environments.
Features
Operating temperature: -55 to 135°C
Minimum full recovery temperature: 125°C
Shrink ratio: 2:1
Compliant Standard GJB 1217A-2009
Dimension
| Size | As supplied(mm) | After recovered (mm) |
Standard length (m) |
||
| S13 |
Inner diameter D (min.) |
Wall thickness T |
Inner diameter d (max.) |
Wall thickness t |
|
| 1.5/0.8 | 1.5 | 0.15±0.10 | 0.8 | 0.30±0.08 | 200 |
| 2.4/1.2 | 2.4 | 0.15±0.10 | 1.2 | 0.30±0.08 | 200 |
| 3.2/1.6 | 3.2 | 0.15±0.10 | 1.6 | 0.30±0.08 | 200 |
| 4.8/2.4 | 4.8 | 0.15±0.10 | 2.4 | 0.30±0.08 | 200 |
| 6.4/3.2 | 6.4 | 0.20±0.10 | 3.2 | 0.40±0.08 | 200 |
| 9.5/4.8 | 9.5 | 0.25±0.10 | 4.8 | 0.50±0.08 | 100 |
| 12.7/6.4 | 12.7 | 0.30±0.10 | 6.4 | 0.60±0.08 | 100 |
| 19.1/9.5 | 19.1 | 0.35±0.10 | 9.5 | 0.70±0.08 | 100 |
| 25.4/12.7 | 25.4 | 0.40±0.12 | 12.7 | 0.80±0.12 | 50 |
| 31.8/15.9 | 31.8 | 0.45±0.12 | 15.9 | 0.90±0.12 | 50 |
| 38.1/19.1 | 38.1 | 0.50±0.15 | 19.1 | 1.00±0.15 | 50 |
| 50.8/25.4 | 50.8 | 0.55±0.15 | 25.4 | 1.10±0.15 | 50 |
Technical Data (GJB 1217A-2009)
| Property | Test Method | Requirement | |||
| Longitudinal change | -- | -5%~5% | |||
| Restricted Shrinkage | 175°C/30min | No cracking | |||
| Water absorption | 23°C/24h | ≤0.5% | |||
| Tensile Strength | 500mm/min | ≥10.4MPa | |||
| Ultimate Elongation | 500mm/min | ≥200% | |||
| Heat shock | 250°C/4h | No cracking, dripping or flowing | |||
| Heat Aging Tensile Strength Ultimate Elongation |
175°C/168h |
Not less than 70% value before test ≥100% |
|||
| Dielectric strength | -- | ≥19.7kV/mm | |||
| Dielectric withstand | AC 2500V, 60s | No breakdown | |||
| Volume resistivity | -- | ≥1.0×1014Ω·cm | |||
| Fluid resistance Tensile Strength Dielectric strength |
23°C/24h |
Not less than 70% value before test ≥ 15.8kV/mm |
|||
| Flammability (colors only) | -- | 60 second maximum burning duration | |||
| Copper corrosion | 175°C/16h | No Corrosion | |||
| Low-temperature flexibility | -55°C/4h | No Cracking | |||
| Thermal cycling Tensile Strength Ultimate Elongation |
-55°C/135°C/10 cycles |
Not less than 70% value before test ≥ 100% |
|||
| Salt spray test Tensile Strength Ultimate Elongation |
GJB 150.11 |
Not less than 70% value before test ≥ 100% |
|||
| Damp-heat test Tensile Strength Ultimate Elongation |
GJB 150.9 |
Not less than 70% value before test ≥ 100% |
|||
| Fungus Resistance | GJB 150.10 | No worse than rating 1 | |||
| Vacuum Outgassing | GJB 1217A-2009 Method 4001 | TML ≤1% CVCM ≤0.11% |
|||
| Radiation Resistence | GJB 178A Method 1019 | The irradiation dose is 200krad(Si), and the surface is not cracked, damaged or brittle | |||