IDS-135 Polyolefin Heat Shrink Marker Sleeve
IDS-135
$0.00
IDS-135 Polyolefin Heat Shrink Marker Sleeve Introduction Military grade,flexible,high flame-retardant, electrical insulation, chemical resistance.Excellent print performance,easy identification.The identification meets military standard requirements for abrasion and solvent resistance, ensuring...
IDS-135 Polyolefin Heat Shrink Marker Sleeve
Introduction
Military grade,flexible,high flame-retardant, electrical insulation, chemical resistance.Excellent print performance,easy identification.The identification meets military standard requirements for abrasion and solvent resistance, ensuring permanent identification.Ladder format and continuous tubes both are available.
Features
Operating temperature: -55 to 135°C
Minimum full recovery temperature: 135°C
Shrink ratio: 2:1 & 3:1
Compliant Standard GJB 7277-2011
Compliant Standard UL224
Standard Color: See the below for details
Dimension
| Part No. IDS-135 |
As supplied(mm) | After recovered(mm) | |||||
| Inner | Sleeve | Sleeve | Inner | Wall thickness |
|||
| diameter D(min.) |
Flattened Width W(min. |
Progression ) (nom.) |
diameter d(max.) |
||||
| Shrink ratio 2:1 | |||||||
| IDS-135-M-2X-1.6-* | 1.6 | 3.2 | 10.3 | 0.8 | 0.45±0.08 | ||
| IDS-135-M-2X-2.4-* | 2.4 | 4.3 | 12.7 | 1.2 | 0.50±0.10 | ||
| IDS-135-M-2X-3.2-* | 3.2 | 5.8 | 12.7 | 1.6 | 0.50±0.10 | ||
| IDS-135-M-2X-4.8-* | 4.8 | 8.0 | 12.7 | 2.4 | 0.55±0.11 | ||
| IDS-135-M-2X-6.4-* | 6.4 | 10.7 | 16.9 | 3.2 | 0.55±0.11 | ||
| IDS-135-M-2X-9.5-* | 9.5 | 15.5 | 25.4 | 4.8 | 0.60±0.12 | ||
| IDS-135-M-2X-12.7-* | 12.7 | 20.4 | 27.9 | 6.4 | 0.60±0.12 | ||
| IDS-135-M-2X-19.1-* | 19.1 | 30.5 | 38.1 | 9.5 | 0.70±0.15 | ||
| IDS-135-M-2X-25.4-* | 25.4 | 40.4 | 48.3 | 12.7 | 0.70±0.15 | ||
| IDS-135-M-2X-38.1-* | 38.1 | 60.3 | 70.0 | 19.1 | 0.70±0.15 | ||
| IDS-135-M-2X-50.8-* | 50.8 | 80.0 | 96.5 | 25.4 | 0.73±0.15 | ||
| IDS-135-M-2X-76.2-* | 76.2 | 114.3 | 137.2 | 38.1 | 0.73±0.15 | ||
| Shrink ratio 3:1 | |||||||
| IDS-135-M-3X-2.4-* | 2.4 | 4.3 | 12.7 | 0.79 | 0.57±0.12 | ||
| IDS-135-M-3X-3.2-* | 3.2 | 5.8 | 12.7 | 1.07 | 0.61±0.12 | ||
| IDS-135-M-3X-4.8-* | 4.8 | 8.0 | 12.7 | 1.57 | 0.67±0.12 | ||
| IDS-135-M-3X-6.4-* | 6.4 | 10.7 | 16.9 | 2.11 | 0.71±0.15 | ||
| IDS-135-M-3X-9.5- | 9.5 | 15.5 | 25.4 | 3.18 | 0.77±0.15 | ||
| IDS-135-M-3X-12.7-* | 12.7 | 20.4 | 27.9 | 4.22 | 0.80±0.15 | ||
| IDS-135-M-3X-19.1-* | 19.1 | 30.5 | 38.1 | 6.35 | 0.84±0.17 | ||
| IDS-135-M-3X-25.4-* | 25.4 | 40.4 | 48.3 | 8.46 | 0.86±0.17 | ||
| IDS-135-M-3X-38.1-* | 38.1 | 60.3 | 70.0 | 12.70 | 0.89±0.18 | ||
| IDS-135-M-3X-50.8-* | 50.8 | 80.0 | 96.5 | 17.00 | 0.90±0.18 | ||
| IDS-135-M-3X-76.2-* | 76.2 | 114.3 | 137.2 | 25.40 | 0.92±0.18 | ||
Technical Data(GJB7277-2011)
| Property | Test Method | Requirement | |||
| Density | ASTM D792 | ≤1.40g/cm³ | |||
| Longitudinal Change | 一 | 2:1-5%~5% | |||
| 3:1-10%~5% | |||||
| Restricted Shrinkage | 175℃/30min | No cracking | |||
| Water Absorption | 23C/24h | ≤0.5% | |||
| Tensile Strength | 500mm/min | ≥10.4MPa | |||
| Ultimate Elongation | 500mm/min | ≥300% | |||
| Heat shock | 225℃/4h | No cracking,dripping or flowing | |||
| Mark Identifiability | After erasing 50 times with an eraser | ||||
| in one direction,mark is legible | |||||
| Heat Aging | 175℃/168h | ||||
| Ultimate Elongation | ≥200% | ||||
| Mark ldentifiability | After erasing 50 times with an eraser | ||||
| in one direction,mark is legible | |||||
| Color Stability | 175℃/24h | No fading or discoloration | |||
| Print Perfomance | Surface characters are era | sedMark is legible | |||
|
50 times in one direction o 30 times back and forth |
r | ||||
| Dielectric Strength | 一 | ≥19.7KV/mm | |||
| Dielectric Voltage Withstand | AC 2500V,60s | No breakdown | |||
| Volume Resistivity | 一 | ≥1.0×10¹⁴Ω·cm | |||
| Fluid resistance | 23°℃/24h | ||||
| Tensile Strength | ≥6.9MPa | ||||
| Dielectric Strength | ≥15.8kV/mm | ||||
| Mark ldentifiability | After erasng 50 tmes with an eraser in | ||||
| one direction,mark is legible | |||||
| Flammability | ≤60 second burning duration | ||||
| Copper Effect | 175℃/16h | No corrosion | |||
| Low-temperature Flexibility -55°℃/4h | No cracking | ||||
| Thermal cycling | -55°℃/135℃/10 cycles | Ultimate Elongation≥200%,After | |||
| erasing 50 times with an erase in one | |||||
| direction,mark is legible | |||||
| Salt spray test | GJB150.11 | Ultimate Elongation≥200%,After | |||
| erasing 50 times with an eraser in one | |||||
| direction,mark is legible | |||||
| Damp-heat test | GJB150.9 |
Ultimate Elongation≥200%,After erasing 50 times with an erase in one |
|||
| direction,mark is legible | |||||
| Fungus Resistance | GJB150.10 | Not less than rate 1 | |||